KJN Quick Drying Series Silica sol

Follows:

Product Types:

Update time:2020-07-27 11:21

product description:The quick-drying silica sol is obtained by polymer-modifying the surface of the silica sol, so that the casting shell mold can establish the wet strength in advance, shortening the drying time of the casting shell mold, thereby improving the casting p...

support hotline:13355002933

PRODOUCT PARAMETER


NO.

Series 

Type

technical parameter 

Stable period

M

 SiO2%

Density

(25℃,g/cm3)

Na2O%

pH
(25℃)

viscosity
(25℃,mpa.s)

Average particle size(nm)

1

Quick Drying
Series silica sol

KJN-830

26~30

1.17~1.20

≤0.5

9.5~10.5

≤9

7~10

6M

2

KJN-1430

28~30

1.18~1.20

≤0.5

9.5~10.5

≤9

10~15

6M

3

KJN-1430-D1

30~32

1.20~1.22

≤0.3

8.5~10

≤15

10~15

6M

Note: Technical parameters can be adjusted and manufactured according to customers'needs.

 

 Product Features

The quick-drying silica sol is obtained by polymer-modifying the surface of the silica sol, so that the casting shell mold can establish the wet strength in advance, shortening the drying time of the casting shell mold, thereby improving the casting production efficiency.

Since the solvent used in the silica sol is water, the dry gelation hardening time of the silica sol shell is related to the degree of stability damage and the rate of water loss. Therefore, the gelation hardening mechanism of the quick-drying silica sol shell is as follows:

First, when the slurry is prepared, the quartz powder or the mullite powder impacts the space network structure of the high molecular molecule, the adsorption of the polymer molecules from the particles, the adsorption layer of the fast-drying silica sol is destroyed, and the colloidal reaction occurs. Produces a very strong gel and moisture. which is:

mSiO2·nH2O→mSiO2·(n-1)H2O+H2O

Second, the desorbed polymer molecules are re-joined together to form a thin layer of high polymer film with cohesiveness. In addition, controlling the humidity and wind speed of the environment, the quick-drying silica sol shell and the silica sol shell also form a humidity gradient with a high inside and outside, and the water accelerates and evaporates, and the gelation hardening time is shortened.

Conditions for use of quick-drying silica sol:

1. This product does not need to change the shell making process during the use process. The requirements for the selection of precision casting powder, coating ratio, temperature and humidity of the shell workshop are similar to those of ordinary silica sol.

 2. Under the same process conditions as ordinary silica sol, the interlaminar drying time is about half of that of ordinary silica sol.

 3. The shell has high wet strength, can withstand low humidity and large wind, and has certain anti-dissolution and anti-cracking ability.


Product application field

This series of products is suitable for precision castings that require high precision and fast drying speed in precision casting.